检查井模具在设计过程中就要非常的注意,保证各个零件的合理,如果设计的模具强度不够,刀口间距太近,模板块数不够无垫板垫脚等的话,都会影响模具的后期使用和损坏。我们在给检查井模具选择材料的时候一定要注意这个问题,不要选择便宜的材料,影响了模具的后期使用。在检查井模具的制作过程中一般都会经过热处理,如果淬火工艺的加工不当的话就会出现模具变形的现象,导致模具无法正常的使用。生产模具的时候,如果需要磨平的位置,研磨不够的话,也会出现变形的问题。除了模具本身需要注意的事项外,在模具使用后也需要适当的保养才能延长模具的寿命。

Check wells mold is very attention in the design process, to ensure that every part of the mould design is reasonable, if the strength is not enough, the distance is too near, not without stepping plate template number etc. it will affect the subsequent use of mold and damage. We must pay attention to this problem when choosing the material for the check well die, and do not choose the cheap material, which affects the later use of the mold. Generally, heat treatment is usually done in the production process of the inspection well. If the quenching process is not processed properly, the phenomenon of die deformation will happen, which will lead to the failure of the mold to be used normally. When the mold is produced, there will be a problem of deformation if the grinding position is needed and the grinding is not enough. In addition to the need to pay attention to the mold itself, the mold needs to be properly maintained after the use of the mold to prolong the life of the mold.